Products & Specifications
|
|
|
| |
TJ-31 ECO
 |
Material
Description and Application
|
Economically
priced general purpose jointing
for low temperature and low
pressure conditions in steam,
water and gas lines.
Non-Metallic
and Metallic
|
|
Recommended
Maximum Operating Temperature
and Pressure
|
Temp
|
Non-Metallic
|
Metallic
|
|
350oC
|
380oC
|
|
Pressure
|
30 kg/cm2
|
35 kg/cm2
|
|
Typical
Properties
(For Non-Metallic
material)
|
Tensile
Strength (Min.) : 60 kg/cm2
Density (nominal) : 1.85 gms/cc
Compression : 6-14%
Recovery (Min.) : 40%
Loss on Ignition (Max.) : 28%
|
|
Specification
Compliance
|
ASTM F104
F112000 M3
|
|
Standard Size
|
1600mm x 1500
mm, 1600mm x 3000mm
|
|
Standard
Thickness
|
0.4mm, 0.5mm,
0.75mm, 1.0mm, 1.5mm, 3.0mm
Other sizes and
thicknesses available on
request.
|
TJ-41 PLUS
  |
Material
Description and Application
|
An alternative
to TJ-31 ECO with better ageing
properties yet economically
priced.
Non-Metallic
and Metallic
|
|
Recommended
Maximum Operating Temperature
and Pressure
|
Temp
|
Non-Metallic
|
Metallic
|
|
350oC
|
380oC
|
|
Pressure
|
30 kg/cm2
|
35 kg/cm2
|
|
Typical
Properties
(For Non-Metallic
material)
|
Tensile
Strength (Min.) : 80 kg/cm2
Density (nominal) : 1.85 gms/cc
Compression : 6-14%
Recovery (Min.) : 40%
Loss on Ignition (Max.) : 28%
|
|
Specification
Compliance
|
IS 2712 / 98 :
Grade W/3
ASTM F104 F112000 M4
|
|
Standard Size
|
1600mm x 1500
mm, 1600mm x 3000mm
|
|
Standard
Thickness
|
0.4mm, 0.5mm,
0.75mm, 1.0mm, 1.5mm, 3.0mm
Other sizes and
thicknesses available on
request.
|
TJ-51 PLUS
 |
Material
Description and Application
|
A medium grade
jointing finding extensive
applications across a wide
industry segment in steam,
water, gas and alkali lines.
Non-Metallic
and Metallic
|
|
Recommended
Maximum Operating Temperature
and Pressure
|
Temp
|
Non-Metallic
|
Metallic
|
|
380oC
|
400oC
|
|
Pressure
|
40 kg/cm2
|
45 kg/cm2
|
|
Typical
Properties
(For Non-Metallic
material)
|
Tensile
Strength (Min.) : 100 kg/cm2
Density (nominal) : 1.9 gms/cc
Compression : 6-14%
Recovery (Min.) : 40%
Loss on Ignition (Max.) : 28%
|
|
Specification
Compliance
|
IS 2712 / 98 :
Grade W/3
ASTM F104 F112700 M4
|
|
Standard Size
|
1600mm x 1500
mm, 1600mm x 3000mm
|
|
Standard
Thickness
|
0.4mm, 0.5mm,
0.75mm, 1.0mm, 1.5mm, 3.0mm
Other sizes and
thicknesses available on
request.
|
TJ-61 EXTRA
  |
Material
Description and Application
|
A versatile
sealing material
specially bonded with
superior compounds to handle
higher temperature and pressure
service conditions in oil, water
and gas pipelines and medium
temperature
oil pipelines
Non-Metallic
and Metallic
|
|
Recommended
Maximum. Operating Temperature
and Pressure
|
Temp
|
Non-Metallic
|
Metallic
|
|
450oC
|
480oC
|
|
Pressure
|
80 kg/cm2
|
90 kg/cm2
|
|
Typical
Properties
(For Non-Metallic
material)
|
Tensile
strength (Min.) :
140 kg/cm2
Density (nominal) : 1.95
gms/cc
Compression : 7-12%
Recovery (Min.) : 40%
Stress Relaxation
(Min. Residual Stress) :
180kg/cm2
Loss on ignition (Max.) : 28%
|
|
Fuel Immersion
Properties
|
Oil No. 3
Increase in mass (Max.) : 30%
Increase in thickness (Max.) :
20%
Fuel B
Increase in mass (Max.) :25%
Increase in thickness (Max.) :
20%
Water
Increase in mass (Max.) :10%
|
|
Specification
Compliance
|
IS 2712 / 98 :
Grade W/2, O/2
ASTM 104F 112441 M6
|
|
Standard Size
|
1600mm x 1500
mm, 1600mm x 3000mm
|
|
Standard
Thickness
|
0.4mm, 0.5mm,
0.75mm, 1.0mm, 1.5mm, 3.0mm
Other sizes and
thicknesses available on
request.
|
TJ-71 SUPER 300
 
|
Material
Description and Application
|
A superior
grade of jointing with specially
selected
chrysotile fibres and heat
resisting compounds
to
handle extreme workings
conditions in superheated and
saturated steam lines as well as
gas, alkali, oil,
solvent, chemical, petrochemical
and dilute acid lines.
Non-Metallic
and Metallic
|
|
Recommended
Maximum Operating Temperature
and Pressure
|
Temp
|
Non-Metallic
|
Metallic
|
|
550oC
|
600oC
|
|
Pressure
|
150 kg/cm2
|
180 kg/cm2
|
|
Typical
Properties
(For Non-Metallic
material)
|
Tensile
strength (Min.) :
250 kg/cm2
Density (nominal) :1.95
gms/cc
Compression : 7-12%
Recovery (Min.) : 40%
Stress Relaxation(Min. Residual
Stress) : 180kg/cm2
Loss on ignition (Max.) : 28%
|
|
Fuel Immersion
Properties
|
Oil No. 3
Increase in mass (Max.) : 20%
Increase in thickness (Max.) :
25%
Fuel B
Increase in mass (Max.) : 20%
Increase in thickness (Max.) :
20%
Water
Increase in mass (Max.) : 10%
|
|
Specification
Compliance
|
IS 2712 / 98 :
Grade W/1
ASTM F104 F112231 M7
|
|
Standard Size
|
1600mm x 1500
mm, 1600mm x 3000mm
|
|
Standard
Thickness
|
0.4mm, 0.5mm,
0.75mm, 1.0mm, 1.5mm, 3.0mm
Other sizes and
thicknesses available on
request.
|
TJ OIL ‘SPECIAL’
  |
Material
Description and Application
|
Manufactured
with specialty rubbers and high
grade fibres to resist the
medium flowing through
petrochemical, hydrocarbon,
solvent and other aromatic
compound pipelines
Non-Metallic
and Metallic
|
|
Recommended
Maximum Operating Temperature
and Pressure
|
Temp
|
Non-Metallic
|
Metallic
|
|
550oC
|
600oC
|
|
Pressure
|
150 kg/cm2
|
180
kg/cm2
|
|
Typical
Properties
(For Non-Metallic
material)
|
Tensile
strength (Min.) : 250 kg/cm2
Density (nominal) : 1.95
gms/cc
Compression : 7-14%
Recovery (Min.) : 45%
Stress Relaxation
(Min. Residual Stress) :
180kg/cm2
Loss on ignition (Max.) : 28%
|
|
Fuel Immersion
Properties
|
Oil No. 3
Increase in mass (Max.) : 15%
Increase in thickness (Max.) :
25%
Fuel B
Increase in mass (Max.) : 20%
Increase in thickness (Max.) :
15%
Water
Increase in mass (Max.) : 10% |
|
Specification
Compliance
|
IS 2712 / 98 :
Grade W/1
IS 2712 / 98 :
Grade O/1
ASTM F104 F112231 M7
|
|
Standard Size
|
1600mm x 1500
mm, 1600mm x 3000mm
|
|
Standard
Thickness
|
0.4mm, 0.5mm,
0.75mm, 1.0mm, 1.5mm, 3.0mm
Other sizes and
thicknesses available on
request.
|
TJ OIL ‘F’
 |
Material
Description and Application
|
A specially
designed variation of TJ Oil
’Special’ having very good
Resistance to all oils and fuels
as
well as steam and water. Ideal
for
sealing engine parts in the
Automobile industry.
Non-metallic
|
|
Recommended
Maximum Operating Temperature
and Pressure
|
Temp
|
Non-Metallic
|
|
450oC
|
|
Pressure
|
50 kg/cm2
|
|
Typical
Properties
(For Non-Metallic
material)
|
Tensile
strength (Min.) :
280 kg/cm2
Density (nominal) : 1.95
gms/cc
Compression : 7-11%
Recovery (Min.) : 45%
Stress Relaxation
(Min. Residual Stress) :
180kg/cm2
Loss on ignition (Max.) : 28%
|
|
Fuel Immersion
Properties
|
Oil No. 3
Increase in mass (Max.) : 20%
Increase in thickness (Max.) :
10%
Fuel B
Increase in mass (Max.) : 20%
Increase in thickness (Max.) :
10%
Water
Increase in mass (Max.) : 10%
|
|
Specification
Compliance
|
IS 2712 / 98 :
Grade O/1
ASTM F104 F112231 M7
|
|
Standard Size
|
1600mm x 1500
mm, 1600mm x 3000mm
|
|
Standard
Thickness
|
0.4mm, 0.5mm,
0.75mm, 1.0mm, 1.5mm, 3.0mm
Other sizes and
thicknesses available on
request.
|
TJ OIL ‘CS’
 |
Material
Description and Application
|
This has been
specially engineered
for applications in following
low or fluctuating torque
pressures or for sealing of
parts having uneven
surfaces, specially in the
Automobile industry.
Non-metallic
|
|
Recommended
Maximum Operating Temperature
and Pressure
|
Temp
|
Non-Metallic
|
|
500oC
|
|
Pressure
|
100 kg/cm2
|
|
Typical
Properties
(For Non-Metallic
material)
|
Tensile
strength (Min.) :
250 kg/cm2
Density (nominal) :1.95
gms/cc
Compression : 7-14%
Recovery (Min.) : 45%
Stress Relaxation
(Min. Residual Stress) :
180kg/cm2
Loss on ignition (Max.) : 28%
|
|
Fuel Immersion
Properties
|
Oil No. 3
Increase in mass (Max.) : 30%
Increase in thickness (Max.) :
25%
Fuel B
Increase in mass (Max.) : 20%
Increase in thickness (Max.) :
25%
Water
Increase in mass (Max.) : 10%
|
|
Specification
Compliance
|
ASTM F104
F112341 M7
|
|
Standard Size
|
1600mm x 1500
mm, 1600mm x 3000mm
|
|
Standard
Thickness
|
0.4mm, 0.5mm,
0.75mm, 1.0mm, 1.5mm, 3.0mm
Other sizes and
thicknesses available on
request.
|
TJ ACID
 |
Material
Description and Application
|
Manufactured
with special grades
of fibres and acid resistant
rubbers to make it
suitable for resisting the
corrosive
action in concentrated organic,
inorganic and mineral acid lines
under varying temperature and
pressure condition.
Non-Metallic
|
|
Recommended
Maximum Operating Temperature
and Pressure
|
Temp
|
Non-Metallic
|
|
220oC
|
|
Pressure
|
150 kg/cm2
|
|
Typical
Properties
(For Non-Metallic
material)
|
Tensile
strength (Min.) :
165 kg/cm2
Density (nominal) :1.95
gms/cc
Compression : 7-11%
Recovery (Min) : 45%
Stress Relaxation
(Min. Residual Stress) :
180kg/cm2
Loss on ignition (Max.) : 28%
|
|
Specification
Compliance
|
IS 2712 / 98 :
Grade A/1
ASTM F104 F112000 M6
|
|
Standard Size
|
1600mm x 1500
mm, 1600mm x 3000mm
|
|
Standard
Thickness
|
0.4mm, 0.5mm,
0.75mm, 1.0mm, 1.5mm, 3.0mm
Other sizes and
thicknesses available on
request.
|
|
|
|
| |
Note :-
- All Tests are related to properties of 1.5
mm thickness material
- Testing is done as per IS 2712 and related
reference standards.
|
|
| |
Disclaimer :- While all
efforts have been made to give the suitable
pressure and temperature conditions and the
properties of our different grades, there are a
host of other factors encountered during the
actual application which determine the choice and
behaviour of the material. The above information
only serves as a guidline for our products.
|
|
【丰胸产品】酒酿鸡蛋丰胸成功的 丰胸案例有没有呢?酒酿蛋作为目前市场上最受欢迎的健康食疗丰胸食物， 粉嫩公主酒酿蛋价格自然是备受瞩目，也少不了很多议论。对于酒酿蛋是否可以丰胸成功，有些姐妹还是存有疑问的 丰胸产品，那么记者今天就采访了酒酿蛋的丰胸经历者，吃了半年酒酿蛋的效果看看她是怎么评价酒酿鸡蛋的丰胸效果的 丰胸产品粉嫩公主。 |